Fluon® ETFE is a copolymer of tetrafluoroethylene and ethylene.

ETFE compound grades are designed for applications where enhanced properties over natural ETFE are required e.g. improved wear resistance, reduced mould shrinkage, improved compressive resistance, increased flexural strength, flexural modulus, improved dimensional stability.

Fluon® ETFE has a wide operating temperature range (-180° to +150°C)

This information sheet contains typical property data which should not be
used for specification purposes.
Fluon® ETFE Compound Grades
 
Grade
MFR
g/10
mins
Filler
Type

Filler
Level
(% by
wt)

Tensile
Strength
(MPa)
Elong.
to break
(%)
Flexural
Strength
(MPa)
Flexural
Modulus
(MPa)
Processing
Applications/
Characteristics
D - 3159
D-638
D-638
D-790
D-790
    
ETFE 10 CF 464-102-515**
TBA
Carbon fibre
10
TBA
TBA
TBA
TBA
Injection moulding & compression moulding
 Improved stiffness (high flexural modulus)
ETFE 20 CF 464-102-506
4
Carbon fibre
20
36
 6
53
2585
Injection moulding & compression moulding
Improved stiffness (high flexural modulus)
CF-8011
6.5 - 9
Carbon fibre
molybdenum
disulphide
10
36
20
36
1800
Injection moulding

Improved abrasion
 
 
 
 
 
 
GF-8025T
3.9 - 9
Glass fibre
25
44
10
65
5700
Injection moulding
Improved
dimensional stability
PM-8015
6.5 - 12
PTFE
15
29
-
23
980
Injection moulding
Lower friction
PM-8015
6.5 - 12
PTFE
15
29
-
23
980
Injection moulding
Lower friction

**ETFE 10 CF 464-102-515 is an experimental grade & data would be available on application at commercial launch.

                                                      Fluon® is a trademark of Asahi Glass Company